Process for manufacturing an anti-ballistic article

ABSTRACT

The invention relates to anti-ballistic articles comprising a stack of sheets, each sheet having one or more mono-layers of polyethylene anti-ballistic fibers and a thermoplastic binder, wherein the specific energy absorption (SEA) of the anti-ballistic article is greater than 145 J/kg/m 2  and the maximum % thickness increase, measured at about 90° C., is less than 8% after storing the article for 160 hours at 90° C.

This application is a divisional of commonly owned copending U.S.application Ser. No. 12/921,467, filed Sep. 8, 2010 (now U.S. Pat. No._______), which is the national phase application under 35 USC §371 ofPCT/EP2009/053864, filed Apr. 1, 2009, which designated the US andclaims benefit of EP Patent Application No. 08006711.9, filed Apr. 2,2008, the entire contents of each of which are hereby incorporated byreference.

The invention relates to a process for the manufacture of ananti-ballistic article formed from a stack of sheets, each sheetcomprising one or more monolayers of anti-ballistic fibers. Theinvention also relates to anti-ballistic articles and the use of vacuumbags in the manufacture of anti-ballistic articles.

There is an increasing demand for anti-ballistic articles which providegreater performance per given areal density. For example, the increasingamount of electronic surveillance equipment which is mounted uponmilitary helmets has lead to the problem of heavy and cumbersome helmetsand consequently a desire for lighter weight helmets which deliver thesame anti-ballistic performance. Further, to provide enhanced ballisticprotection to vehicles there has been a need to increase the thicknessof the anti-ballistic layers to a point where the anti-ballisticlayering is beginning to compromise the maneuverability and handling ofthe vehicle. In addition to increased anti-ballistic performance, thegrowing demand for anti-ballistic articles has also lead to the need forshorter production cycle times to enable increased production capacity.

Anti-ballistic articles may also be frequently exposed to hightemperatures for long durations. It is important that anti-ballisticarticles have sufficient dimensional stability to maintain their shape,such that their functional performance is not compromised. One exampleis anti-ballistic panels positioned adjacent to an automotive engine.Anti-ballistic panels for vehicles are necessarily thick to achieve therequired anti-ballistic performance and even small dimensional changesin the anti-ballistic panels may result in the panels exerting pressureson the vehicle's framework, thus compromising the vehicle's structuralintegrity. Another example is helmets and vests subject to a hotenvironment (e.g. in a vehicle's trunk). Thus, anti-ballistic articlesdesigned for such personal protection which are subjected to a hotenvironment should also have good dimensional stability to ensure thatthey retain a comfortable fit against the wearer's body.

An object of the present invention is to provide an anti-ballisticarticle and a process for the manufacture of an anti-ballistic articlewhich overcomes at least some of the abovementioned problems.

This object is achieved with a process for the manufacture of ananti-ballistic article comprising the steps of

-   -   a. forming a stack of sheets (“a stack”) by stacking 2 or more        sheets, each sheet comprising one or more mono-layers of        anti-ballistic fibers and optionally a thermoplastic binder,        followed by    -   b. subjecting the stack of sheets to a reduced atmospheric        pressure environment; and    -   c. while maintaining the reduced atmospheric pressure        environment, subjecting said stack of sheets to a pressure of at        least 10 MPa at an elevated temperature.

It has been surprising found that the application of a reducedatmospheric pressure environment to the stack whilst the stack iscompressed at an elevated temperature produces a surprising increase inanti-ballistic performance, as measure by the specific energy absorption(SEA) of the material. Preferably, the sheets are unidirectional sheetswhereby in the stack, the direction of the anti-ballistic fibers in amonolayer is at an angle α to the fiber direction in an adjacentmono-layer. However, other assemblies and orientations of fibers mayalso be employed. For example, in another embodiment the sheet is awoven sheet.

The present process solves the problem of providing improvedanti-ballistic performance.

The present invention provides several additional advantages derivedfrom the resultant increase in SEA of the stack:

-   -   1. An anti-ballistic article with increased anti-ballistic        performance relative to conventionally produced anti-ballistic        articles may be produced having the same areal density; and    -   2. A lighter more compact anti-ballistic article may be produced        with the same anti-ballistic performance as a stack produced via        conventional techniques.

In one embodiment of the present invention, there is provided ananti-ballistic article comprising a stack of sheets, each sheetcomprising one or more mono-layers of polyethylene anti-ballistic fibersand a thermoplastic binder, characterized in that the specific energyabsorption (SEA) of the anti-ballistic article is greater than 145J/kg/m² and the maximum % thickness increase, measured at about 90° C.,is less than 8% after storing the article for 160 hours at 90° C.

Preferably the SEA is greater than 147 J/kg/m², more preferably greaterthan 149 J/kg/m²′ even more preferably greater than 151 J/kg/m² and mostpreferably greater than 153 J/kg/m². The maximum % thickness change isless than 7.5%, more preferably less than 7.0%, even more preferablyless than 6.5% and most preferably less than 6.0%.

It has been found that the anti-ballistic articles of the presentinvention may be produced through the application of vacuum and pressureas previously described.

It will be appreciated that different embodiments describing theanti-ballistic article made in reference to the process are alsoapplicable to embodiments describing the anti-ballistic article alone.

Stack

The anti-ballistic article according to the invention comprises a stackof sheets. A sheet may include a woven or a non-woven sheet (i.e feltconstruction) derived from anti-ballistic fibers in addition to a stackof monolayers derived from anti-ballistic fibers.

Preferably, these sheets are unidirectional sheets which comprise one ormore mono-layers of unidirectional oriented anti-ballistic fibers and abinder.

The term mono-layer of unidirectional anti-ballistic fibers refers to alayer of unidirectionally oriented anti-ballistic fibers i.e.anti-ballistic fibers in one plane that are essentially oriented inparallel. Within this aspect of the invention, the direction of thefibers in a monolayer is preferably at an angle a to the direction ofthe fibers in an adjacent mono-layer. The angle a is preferably between5 and 90°, more preferably between 45 and 90° and most preferablybetween 75 and 90°.

The article according to the invention comprises at least 2 sheets,preferably at least 40 sheets, more preferably at least 80 sheets, evenmore preferably at least 120 sheets and most preferably at least 160sheets

The term anti-ballistic fiber comprises not only a monofilament but,inter alia, also a multifilament yarn and a tape.

Fiber Formation

The anti-ballistic fibers in the stack according to the inventionpreferably have a tensile strength of at least about 1.2 GPa (determinedin accordance with ASTM D2256) and a tensile modulus of at least 40 GPa.These fibers preferably have a tensile strength of at least 2 GPa, morepreferably at least 2.5 GPa or most preferably at least 3 GPa. Theadvantage of these fibers is that they have very high tensile strength,so that they are in particular very suitable for use in e.g. lightweightand strong articles.

Preferably the fineness per filament of the anti-ballistic fiber is lessthan 5 denier per filament (dpf), more preferably less than less than 3dpf, even more preferably less than 2 dpf and most preferably less than1.5 dpf.

The anti-ballistic fibers may be inorganic or organic fibers.

Suitable inorganic fibers are, for example, glass fibers, carbon fibersand ceramic fibers.

Suitable organic fibers with such a high tensile strength are, forexample, aromatic polyamide fibers (generally referred to as aramidfibers), especially poly(p-phenylene terephthalamide), liquidcrystalline polymer and ladder-like polymer fibers such aspolybenzimidazoles or polybenzoxazoles, esp.poly(1,4-phenylene-2,6-benzobisoxazole) (PBO), orpoly(2,6-diimidazo[4,5-b-4′,5′-e]pyridinylene-1,4-(2,5-dihydroxy)phenylene)(PIPD; also referred to as M5) and fibers of, for example, polyolefinsas e.g. polyethylene and polypropylene, polyvinyl alcohol, andpolyacrylonitrile which are highly oriented, such as obtained, forexample, by a gel spinning process.

More preferably aromatic polyamide fibers, especially poly (p-phenyleneterephthalamide), liquid crystalline polymer and ladder-like polymerfibers such as polybenzimidazoles or polybenzoxazoles, especially poly(1,4-phenylene-2,6-benzobisoxazole) orpoly(2,6-diimidazo[4,5-b-4′,5′-e]pyridinylene-1,4-(2,5-dihydroxy)phenylene)and ultra high molecular weight polyethylene are used as anti-ballisticfiber.

In one embodiment of the present invention, the anti-ballistic fibersconsist of ultra high molecular weight (UHMWPE) filaments that have beenprepared by a gel spinning process, such as described, for example, inGB 2042414 A, WO 01/73173 or in “Advanced Fibre Spinning Technology”,Ed. T. Nakajima, Woodhead Publ. Ltd (1994), ISBN 185573 182 7. The useof these UHMWPE fibers results in a very good anti-ballistic performanceper unit of weight. A gel spinning process essentially consists ofpreparing a solution of a linear polyethylene with a high intrinsicviscosity, spinning the solution into filaments at a temperature abovethe dissolving temperature, cooling down the filaments to below thegelling temperature, such that gelling occurs, and stretching thefilaments before, during or after the removal of the solvent.

In gel spinning embodiments, preferably linear polyethylene is used.Linear polyethylene is herein understood to mean polyethylene with lessthan 1 side chain per 100 C atoms, and preferably with less than 1 sidechain per 300 C atoms; a side chain or branch generally containing atleast 10 C atoms. Side chains may suitably be measured by FTIR on a 2 mmthick compression moulded film, as mentioned in e.g. EP 0269151. Thelinear polyethylene may further contain up to 5 mol % of one or moreother alkenes that are copolymerisable therewith, such as propene,butene, pentene, 4-methylpentene, octene. Preferably, the linearpolyethylene is of high molar mass with an intrinsic viscosity (IV, asdetermined on solutions in decalin at 135 degrees (° C.) of at least 4dl/g; more preferably of at least 8 dl/g, most preferably of at least 10dl/g. Such polyethylene is also referred to as ultra-high molar masspolyethylene. Intrinsic viscosity is a measure for molecular weight thatcan more easily be determined than actual molar mass parameters likeM_(n) and M_(w). There are several empirical relations between IV andM_(w), but such relation is highly dependent on molecular weightdistribution. Based on the equation M_(w)=5.37×10⁴ [IV]¹ ³⁷ (see EP0504954 A1) an IV of 4 or 8 dl/g would be equivalent to M_(w) of about360 or 930 kg/mol, respectively.

The weight per unit area of the anti-ballistic fiber in the sheet ormonolayer preferably ranges form 5 to 250 g/m², more preferably rangesform 10 to 200 g/m², most preferably ranges form 20 to 150 g/m².

In the process according to the invention the stack may be made startingfrom sheets comprising a single monolayer instead of sheets (preferablyunidirectional sheets) formed from 2 or more monolayers. However, sheetscomprising single monolayers are difficult to handle, in that theyeasily tear in the fibre direction. It is therefore preferred to makethe stack from consolidated monolayer packages or sheets containing from2 to 8, typically 2, 4 or 8, monolayers that are placed at an angle withrespect to the fibre direction, e.g. cross-wise. Consolidated isintended to mean that the monolayers are firmly attached to one another,so that the monolayers do not delaminate under normal use conditions atroom temperature.

The fibers may also be orientated to form a woven or non-woven sheet.

The sheets of the present invention can be made with different methods,for example by calendaring between rolls, or by compression moulding.Very good results are achieved if also the monolayer packages (i.e.sheet or sheets comprising monolayers) are compressed at an elevatedtemperature, optionally at high pressure, and subsequently cooled undera high pressure; preferably of at least 5 MPa, even more preferablyunder the same pressure as during the previous step. If the economicspermit, the formation of the unidirectional sheets may also be achievedusing the combination of vacuum and high pressure within the scope ofthe present invention.

Flat Tape Formation

In a special embodiment of the present invention, the anti-ballisticfiber is a tape. The tape is preferably derived from polyolefin. A tape(or a flat tape) for the purposes of the present invention is a fiberwith the cross sectional aspect ratio of at least 5:1, more preferablyat least 20:1, even more preferably at least 100: 1 and yet even morepreferably at least 1000:1. The width of the flat tape is preferablybetween 1 mm and 600 mm, more preferable between 1.5 mm and 400 mm, evenmore preferably between 2 mm and 300 mm, yet even more preferablybetween 5 mm and 200 mm and most preferably between 10 mm and 180 mm.Thickness of the flat tape preferably is between 10 μm and 200 μm andmore preferably between 15 μm and 100 μm.

In embodiments in which the anti-ballistic fiber is a flat tape, theflat tape may be prepared in the form of films. A tape may include or bederived from a film. A preferred process for the formation of such filmsor tapes comprises feeding a polymeric powder between a combination ofendless belts, compression-moulding the polymeric powder at atemperature below the melting point thereof and rolling the resultantcompression-moulded polymer followed by drawing. Such a process is forinstance described in EP 0 733 460 A2, which is incorporated herein byreference. If desired, prior to feeding and compression-moulding thepolymer powder, the polymer powder may be mixed with a suitable liquidorganic compound having a boiling point higher than the melting point ofsaid polymer. Compression moulding may also be carried out bytemporarily retaining the polymer powder between the endless belts whileconveying them. This may for instance be done by providing pressingplatens and/or rollers in connection with the endless belts. PreferablyUHMWPE is used in this process. This UHMWPE needs to be drawable in thesolid state. Examples of commercial available solid state drawableUHMWPE includes GUR 4150™, GUR 4120™, GUR 2122™, GUR 2126™ manufacturedby Ticona; Mipelon XM 220™ and Mipelon XM 221U™ manufactured by Mitsui;and 1900™, HB312CM™, HB320CM™ manufactured by Montell.

Another preferred process for the formation of films comprises feeding apolymer to an extruder, extruding a film at a temperature above themelting point of the film and drawing the extruded polymer film. Ifdesired, prior to feeding the polymer to the extruder, the polymer maybe mixed with a suitable liquid organic compound, for instance to form agel, such as is preferably the case when using ultra high molecularweight polyethylene.

Preferably the polyethylene films are prepared by a gel process whichhas been previously described in relation to fiber formation. In short,the gel spinning process, in relation to tape formation, comprisespreparing a solution of a polyolefin of high intrinsic viscosity,extruding the solution into a film at a temperature above the dissolvingtemperature, cooling down the film below the gelling temperature,thereby at least partly gelling the film, and drawing the film before,during and/or after at least partial removal of the solvent.

Drawing, preferably uniaxial drawing, of the produced films may becarried out by means known in the art. Such means comprise extrusionstretching and tensile stretching on suitable drawing units. To attainincreased mechanical strength and stiffness, drawing may be carried outin multiple steps. In case of the preferred ultra high molecular weightpolyethylene films, drawing is typically carried out uniaxially in anumber of drawing steps. The first drawing step may for instancecomprise drawing to a stretch factor of 3. Multiple drawing maytypically result in a stretch factor of 9 for drawing temperatures up to120° C., a stretch factor of 25 for drawing temperatures up to 140° C.,and a stretch factor of 50 for drawing temperatures up to and above 150°C. By multiple drawing at increasing temperatures, stretch factors ofabout 50 and more may be reached. This results in high strength tapes,whereby for tapes of ultra high molecular weight polyethylene, thestrength range is preferably 1.2 GPa to 3 GPa and higher strength mayeasily be obtained.

In embodiments in which the fiber is a tape, the tape may be orientatedto form a woven sheet in addition to a unidirectional monolayer orsheet.

Thermoplastic Binder

The sheets preferably comprise a thermoplastic binder, particularly inembodiments in which the sheets are unidirectional sheets. The termbinder refers to a material that binds or holds the anti-ballisticfibers together in the monolayer or sheet. The binder may enclose theanti-ballistic fibers in their entirety or in part, such that thestructure of the monolayer is retained during handling and making ofsheets. The binder may be applied in various forms and ways; for exampleas a thin layer film (by melting hereof at least partially covering theanti ballistic fibers), as a transverse bonding strip or as transversefibers (transverse with respect to unidirectional fibers), or byimpregnating and/or embedding the fibers with a matrix material, e.g.with a polymer melt, a solution or a dispersion of a polymeric materialin a liquid. Preferably, matrix or binder material is homogeneouslydistributed over the entire surface of the monolayer, whereas a bondingstrip or bonding fibers may be applied locally. Suitable binders aredescribed in e.g. EP 0191306 B1, EP 1170925 A1, EP 0683374 B1 and EP1144740 A1.

The advantage of a thermoplastic binder is that the binder emits a lowlevel of volatile gases, especially at elevated temperatures.

Preferably, the binder is a thermoplastic material with an elongation atbreak of preferably greater than the elongation of the fibers. Thebinder preferably has an elongation of 2 to 600%, more preferably anelongation of 4 to 500%. Suitable thermoplastic binder materials areenumerated in, for example, WO 91/12136 A1 (pages 15-21). Preferredthermoplastic materials are thermoplastic polymer polyurethanes,polyvinyls, polyacrylics, polyolefins or thermoplastic elastomeric blockcopolymers such as polyisopropene-polyethylene-butylene-polystyrene orpolystyrene-polyisoprene-polystyrene block copolymers are preferablyselected as binder material.

In one embodiment, the binder consists of a thermoplastic polymer, whichpreferably completely coats the individual filaments of said fibers in amono-layer, and which binder has a tensile modulus (determined inaccordance with ASTM D638, measured at 25° C. of at least 250 MPa, morepreferably of at least 400 MPa. Such a binder has a reduced release ofvolatile gases compared to thermosetting polymers. As a result, theabsolute pressure in the reduced atmospheric environment may bemaintained more readily.

In an alternative embodiment, the binder consists of a thermoplasticpolymer with a tensile modulus (determined in accordance with ASTM D638,measured at 25° C.) of at less than 250 MPa, more preferably less than100 MPa, even more preferably less than 40 MPa, yet even more preferablyless than 20 MPa and most preferably less than 2 MPa.

Preferably, the binder is applied as a dispersion in water. Examples ofsuitable binder materials include: acrylates, polyurethanes, modifiedpolyolefins and ethylene vinyl acetate.

Impregnation of the reinforcing fibres with the thermoplastic bindermaterial can for instance be effected by applying one or more thin layerfilms of the thermoplastic to the top, bottom or both sides of the planeof the fibres and then passing these, together with the fibres, throughheated pressure rolls. Preferably, however, the fibres, after beingoriented in parallel fashion in one plane, are coated with an amount ofa liquid substance containing the thermoplastic binder material of themonolayer. The advantage of this is that more rapid and betterimpregnation of the fibres is achieved. The liquid substance may be forexample a solution, a dispersion or a melt of the thermoplastic. If asolution or a dispersion of the thermoplastic is used in the manufactureof the monolayer, the process also comprises evaporating the solvent ordispersant.

Alternatively, the binder may be applied locally across theanti-ballistic fibers, thereby minimising the amount of binder usedwhilst enabling the anti-ballistic fibers to be sufficiently stable forhandling and processing, which the stack of sheets undergoes in thesubsequent vacuumisation step.

The amount of binder in the sheet is preferably at most 30 wt. %, morepreferably at most 20 wt. %, even more preferably at most 15 wt. % andmost preferably less than 10 wt. %, relative to the total weight of theanti-ballistic fibers and the binder in the stack. To provide sufficientstability within the sheet, the sheet preferably comprises at least 3wt. % and more preferably at least 5 wt. % binder relative to the totalweight of the anti-ballistic fibers and the binder in the stack. In someembodiments of the present invention, no additional binder is requiredto be added to the fibers. For instance, stacks derived from woven flattape sheets may be sufficiently stable to be processed without requiringadditional binders. In general, the lower the binder content, the higherthe SEA of the stack of unidirectional sheets.

The stack according to the invention has a weight, in this applicationalso referred to as areal density, which spreads over a wide range,encompassing both flexible and rigid constructions. Beneficial effectsof the application of vacuum in accordance with the present inventionhave been observed down to levels of about 2.0 kg/m² or even less.However, it is preferably that the stack has an areal density of atleast 6.0 kg/m², more preferably of at least 8.0 kg/m². In alternativeembodiments, such as those relating to stacks used in armoured vehicles,areal densities of at least 15 kg/m², more preferably at least 20 kg/m²and even more preferably at least 30 kg/m² are used.

Higher areal densities achieved through the use of a higher number ofmonolayers or sheets in the stack have been found to produceparticularly good anti-ballistic performance under the scope of thepresent invention.

Reduced Atmospheric Pressure Environment

The fact that the application of a reduced atmospheric pressureenvironment in combination with high pressure according to the presentinvention was found not to measureably change the density of the stackcompared to the application of high pressure alone, makes the resultanttechnical effect even more unexpected.

A reduced atmospheric pressure environment means an environment in whichthe atmospheric pressure is less than one atmosphere (approximately 0.1MPa). To subject the stack to a reduced atmospheric environment asuction or vacuum source is connected to an enclosure defining thereduced atmospheric pressure environment.

Preferably, the enclosure is formed from a flexible material such thatwhen vacuum is applied to the enclosure, the flexible material is drawnaround the stack, thereby stabilising and preventing relative movementbetween the sheets forming the stack. By securing the stack within theflexible material, the stack may be handled and transported quickly andefficiently during the production cycle. This has the advantage ofspeeding up production and/or enabling lower amounts of binder to beused to stabilize the stack.

In one embodiment, the stack is placed in a vacuum bag to enable avacuum source, such as a vacuum pump, to reduce the atmospheric pressurewithin the vacuum bag to below atmospheric pressure. The vacuum bag ispreferably configured such that it encompasses the stack in full so thatvacuum can be applied to the stack through a vacuum port. The vacuum bagis preferably a flexible polymeric sheet which fully encompasses themoulded article and which comprises an opening or vacuum port from whichsuction is applied to the gaseous environment within the vacuum bag.However, in some embodiments, the reduced atmospheric pressureenvironment is a vacuum chamber defined by a vacuum bag in combinationwith a rigid surface, such as a mould.

Preferably, the vacuum port is formed in-situ (e.g. the vacuum bag isformed by heat sealing a polymeric sheet, with a hole in the vacuum bagleft to serve as the vacuum port) and subsequently sealed after vacuumhas been applied to the vacuum bag. In an exemplary embodiment, thevacuum bag is formed from at least one polymeric sheet. The at least onepolymeric sheet may be preformed into a vacuum bag or formed in-situ.Where the vacuum bag is formed in-situ, two surfaces of the polymericsheet are clamped around the stack to form an enclosure comprising avacuum port. After vacuum is applied to the stack through the vacuumport, the enclosure is preferably heat sealed, thereby forming thevacuum bag.

The vacuum bags are preferably made from a polymeric sheeting materialhaving a melting temperature above the vacuum bag processingtemperature, such as polyethylene, especially low density polyethylene,polypropylene, polyester or polyamide. Multilayered laminateconstructions may also be used. For example, a tri-layered polymerlaminate consisting of a low density polyethylene layer, a polyamidelayer and a interfacial “tie” layer which has favourable rheologicalcharacteristics to enable the low density polyethylene layer and thepolyamide layer to be extruded into a laminate film. In a furtherembodiment, a layer of the laminate forming at least part of the vacuumbag comprising an aluminum foil layer, which functions as a flamebarrier.

The vacuum bag may be designed for single or multi-use application withthe composition and thickness of the vacuum bag being modified by meansknown in the art. Single use vacuum bags are preferred when the vacuumbag is designed to form part of the final anti-ballistic article or whenthe vacuumization step and the compression step are performed atdifferent locations, thereby making the re-use of bags uneconomical.

In a special embodiment, the vacuum bag is made from a polymericsheeting material having a melting temperature at or below a maximumvacuum bag processing temperature (step c). Preferably, the polymericsheet has a melting point no more than 10 degrees Celsius (° C.) andmore preferably no more than 5° C. below the maximum vacuum bagprocessing temperature (step c). It has been unexpectedly found thatvacuum bags having a melting temperature at or below the vacuum bagmaximum processing temperature are still able to produce the technicaleffect attributable to the present invention.

In a preferred embodiment, the vacuum bag forms an integral part of theanti-ballistic article during processing. With the outer layer of thestack comprising a polymeric sheet of the vacuum bag, additionalfunctional properties may be added to the outer surface of theanti-ballistic article. In particular, the printability of the outerlayer may be enhanced through applying a vacuum bag made from apolymeric material of good printability or of a polymeric material whichhas been treated (e.g. corona discharge) to enhance is printability.

The vacuum bag may be also produced from at least one printed polymericsheet, such that the anti-ballistic article obtains a printed outerlayer through the integration of at least one surface of the vacuum bagonto an outer surface of the anti-ballistic article. The integration ofthe vacuum bag onto the surface of the anti-ballistic article has theadvantage of reducing the processing time to produce the final articleby eliminating at least one post compression cycle processing step.

The vacuum bag may be integrated onto the outer surface of the mouldedarticle through use of vacuum bag material which forms an integral bondwith the outer surface of the stack, while still forming an integralseal such that vacuum is maintained during the application of the highpressure cycle. This may be achieved through the use of a binding oradhesive agent to bond a surface of the vacuum bag onto a surface of theanti-ballistic article. Alternatively, the vacuum bag may be made from amaterial which has a softening point below the maximum processingtemperature (step c), such that the material binders to the outersurface during processing. Preferably, the softening point of the vacuumbag material is at no more than 40° C., more preferably no more than 30°C. and most preferably no more than 20° C. below the maximum processingtemperature (step c). Preferably, a heat activated adhesive is precoatedonto an inner surface of the vacuum bag with the heated compressioncycle activating the adhesive thereby forming a bond between a surfaceof the vacuum bag and an outer surface of the anti-ballistic article.

Alternatively, at least a side or a portion of the vacuum bag maycomprise a polymeric composition which has a melting temperature belowthe maximum compression cycle temperature, whereby during thecompression cycle at least a side or portion of the vacuum bag thermallyfuses onto an outer layer of the anti-ballistic article.

In operation, a stack is inserted into a vacuum bag, as previouslydescribed, with a vacuum source applied to the contents of the vacuumbag. Preferably, the absolute gaseous pressure in the reducedatmospheric pressure environment is no more than 0.01 MPa. Morepreferably, the absolute gaseous pressure in the reduced atmosphericpressure environment is no more than 0.005 MPa even more preferably nomore than 0.001 MPa and most preferably no more than 0.0005 MPa. Ingeneral, lower pressure levels correspond to increased anti-ballisticperformance. The vacuum level is measured from a vacuum gauge or othermeasurement means which is typically attached to the vacuum source.

To reach the required absolute pressure, the reduced atmosphericpressure environment is attached to a vacuum source for preferably atleast 20 seconds, more preferably at least 60 seconds and mostpreferably at least 180 seconds. The exact vacuumisation time willdepend upon the configuration of the vacuum port, vacuum bag and stack.For instance, in embodiments in which the anti-ballistic article isformed from a high number of unidirectional sheets (eg. greater than100), then a longer time may be required to ensure that an equilibriumlevel has been reached in terms of the gaseous pressure throughout thereduced atmospheric pressure environment (i.e. the pressure issubstantially the same throughout the bag). The exact vacuumisation timemay be determined through routine experimentation by those skilled inthe art.

The vacuum processing step (b) may be undertaken in a dedicated vacuumpress, in which the stack is placed in a vacuum bag comprising a vacuumport and placed in the vacuum press. The vacuum bag is then enclosed ina chamber which is subjected to a reduced atmosphere. Upon completion ofthe vacuuming step, the vacuum port is preferably heat sealed and thebagged stack removed from the press.

An advantage of this embodiment using a dedicated vacuum press is thatnumber of stacks may be vacuum pressed in advance to ensure productivityof the high pressure processing equipment is maximized. Indeed, thestacks may be vacuum packed, stored and transported to a differentproduction facility to undergo the compression cycle in a dedicated highpressure press. As a result, the stack may be under vacuum, prior to thecompression cycle, from as little as 30 seconds to no more than 3,hours, preferably no more than 4 hours and in some embodiments no morethan 2 days, and preferably no more than 3 days or more.

An advantage of having the stacks vacuum packed is that monolayers orpreformed integral stacks of monolayers may be secured into positionwith a lower reliance on binder materials and/or careful handling. As aconsequence, improved production speeds and improved anti-ballisticperformance may be achieved simultaneously.

Alternatively to using a dedicated vacuum press, the stack may beexposed to the reduced atmospheric gas environment within a vacuumchamber, which forms part of the pressurizing means, such as a hydraulicpress.

In embodiments in which the stack is only partially covered by thevacuum bag, the vacuum bag is preferably attached to a component of themoulding apparatus, such that the stack is fully encompassed by thecombination of a flexible sheet from the vacuum bag or cover and a rigidsurface of the moulding apparatus. Preferably vacuum apertures or portsare evenly distributed over the base of the moulding apparatus. An evendistribution of apertures avoids an uneven distribution of vacuum overthe stack. In some embodiments, the vacuum apertures are connected tovacuum a cavity inside the moulding apparatus which are connected withstop reverse sealed valves and vacuum tubing for connecting to a vacuumpump.

In a further embodiment of the present invention there is provided useof vacuum in the manufacture of anti-ballistic articles, especiallyanti-ballistic articles derived from anti-ballistic fibers. Preferably,the use of vacuum is achieved using a vacuum bag as previouslydescribed.

In a preferred embodiment, the consolidation step (c) is conducted aspart of a compression cycle as follows:

Compression Cycle

After the stack has been placed in the reduced pressure environment, thestack preferably undergoes a compression cycle at an elevatedtemperature. Compression at an elevated temperature is intended to meanthat the stack is subjected to a given pressure for a particularcompression time at a compression temperature sufficiently high suchthat the modulus of the binder is sufficiently low (e.g. temperature isabove the glass transition or melting temperature of the binder), butbelow the softening or melting point of the fibers. The requiredcompression time and compression temperature depend on the kind of fiberand binder and on the thickness of the moulded article and can bereadily determined by one skilled in the art. The temperature duringmelting or reacting generally is chosen below the temperature at whichthe anti-ballistic fiber looses its high mechanical properties due toe.g. melting.

The first step in the compression cycle is to preheat the stack to atemperature sufficient to enable the consolidation of the stack (i.e.good adhesion between sheets).

In embodiments in which the stack is formed from anti-ballistic fiberswith a relatively low melting point, such as polyolefins, the stack ispreheated to a temperature of typically at least 10° C., preferably atleast 20° C. and more preferably at least 25° C. below the meltingtemperature of the anti-ballistic fiber.

In the case of UHMWPE fibers, often having a melting temperature of 155°C., a temperature below 145° C. generally will be chosen and morepreferably below 135° C. The minimum temperature generally is chosensuch that a reasonable speed of consolidation is obtained. In thisrespect 50° C. is a suitable lower temperature limit, preferably thislower limit is at least 75° C., more preferably at least 95° C., mostpreferably at least 115° C. In an exemplary embodiment, the stacksderived from UHMWPE fibers are heated to a temperature of between 120°C. to 130° C. The preheating step typically takes place over a period of10 minutes to 2 hours depending upon the specific heat transferparameters inherent in the materials used.

The second step in the compression cycle is a high pressure compressionstep, in which the stack is compressed by a pressuring means under aload of at least 10 MPa, more preferably at least 12 MPa, morepreferably at least 15 MPa, even more preferably at least 20 MPa, yeteven more preferably at least 25 MPa and most preferably at least 30MPa. The compression cycle is typically initiated before the first stepis complete (i.e the temperature of the stack is still increasing). Thetime the stack is exposed to the high pressure conditions is generallybetween 5 and 100 minutes, depending upon the processing conditions,such as temperature, pressure, composition and number of unidirectionalsheets in the stack.

The third step in the compression cycle is the subsequent cooling of thestack to a temperature below 100° C., preferably below 80° C. and morepreferably below 60° C. In a preferred embodiment, the stack is cooledwhile still under pressure, preferably of at least 5 MPa, morepreferably under the same pressure as in the preceding pressing step.

The anti-ballistic article obtained by the process of the presentinvention is preferably a curved moulded article, such as a helmet or anarmoured plate which conforms to the contours of a vehicle's panel.

In embodiments in which the anti-ballistic article is a curved article,step (c) further comprising placing the stack in a mould, whereinconsolidating of the stack takes place, and the mould is at least partlypressurized by the pressurizing means. The mould comprises at least onemould part in the form of the curved or shaped article—either conformingwith the top surface and/or the bottom surface of the stack—and/or aperipheral mould part.

The resultant anti-ballistic article possesses excellent anti-ballisticperformance.

The invention also relates to an anti-ballistic article obtainableaccording to the process used to produce it as previously described. Inparticular, the anti-ballistic articles, as previously described, showdistinct technical features compared to conventional anti-ballisticarticles.

For the purposes of the present invention, pressure is denoted in unitsof Mega Pascal (MPa) or bar, in which 1 MPa is taken to equal 10 bar.

EXAMPLES Example 1

A stack of 73 unidirectional sheets (about 40 cm by about 40 cm) eachconsisting of two monolayers disposed cross-wise at an angle of 90degrees. The anti-ballistics fibres were highly-drawn fibres of UHMWPEwith a strength of about 36 cN/dtex, a modulus of about 1180 cN/dtex anda fineness of about 2 denier per filament with a cross-section aspectratio of about 1. Each monolayer contains 20 wt. % binder, relative tothe total weight of the monolayer, consisting of astyrene-isoprene-styrene triblock copolymer composition having a tensilemodulus value of about 1 MPa at 25° C. determined in accordance withASTM D638 (available from Kraton Polymers), which is applied as anaqueous dispersion. The areal density of the unidirectional sheet was265 g/m². The areal density of the stack/anti-ballistic article wasabout 19 kg/m².

The stack was placed into a polyamide 6 vacuum bag with a reducedatmospheric pressure of about 5 mBar (5 ×10⁻⁴ MPa) applied to the stackby means of a vacuum pressure applied from a stand alone apparatusdesigned to vacuum seal articles in a polymeric film. Suction wasthrough the opening of the vacuum bag for approximately 25 seconds priorto the bag being heat sealed and removed from the vacuum source.

The stack sealed in a reduced atmospheric pressure environment was thentransferred to a heated hydraulic press. The stack was heated to above60° C. prior to a pressure of 300 bar (30 MPa) being applied to thestack for about 45 minutes at which the maximum temperature reached wasapproximately 125° C. While the 300 bar pressure was maintained thetemperature was decreased to less than 80° C. prior to the opening ofthe press and the removal of the stack. Upon further cooling, thestack/anti-ballistic article was removed from the bag.

Comparative Experiment A

The stack of comparative experiment A (equivalent in composition andstructure to the stack of Example 1) was processed in the same way asthe stack of Example 1 with the exception that:

-   -   the stack was not placed in a vacuum bag and was not subjected        to a reduced atmospheric pressure environment; and    -   prior to the application of the 300 bar pressure, the stack was        subjected to a degassing step for 5 minutes. The degassing step        was conducted by compressing the stack to a pressure of 10 bar,        reduce the pressure by opening the mould (whereby the stack        experiences atmospheric pressure) and wait for 5 minutes before        the application of the 300 bar pressure.

Examples 2 to 3

Example 2 is a repeat of Example 1; Example 3 is the same as Example 1,except that the consolidation pressure was 165 bar.

Comparative Experiments B, C, D and E

Comparative experiment B is a repeat of Comparative experiment A.Comparative experiments C, D and E are equivalent to Comparativeexperiment A but were compressed using different pressures, and in onecase also by using vacuum.

The conditions were as follows:Comparative experiment B at 30 MPa pressure,Comparative experiment C at 16.5 MPa,Comparative experiment D at 2.0 MPa (with vacuum: 5 mbar) andComparative experiment E at 2.0 MPa (without vacuum).

Except for the comparative experiment E, all experiments were performedin duplicate.

The results of the examples and comparative experiments are provided inFIG. 1. Duplicate test results are indicated as, for example,comparative experiment B by the labels B-1 and B-2.

Density

The density of the samples was determined by weighing approximately 50grams of each sample in duplicate and immersing the samples in ethanoland measuring the displacement volume of ethanol. The density was thendetermined by dividing the weight of the samples by its volume, with anaverage of the duplicate reported in table 1.

Ballistic Performance

Stacks in the form of armoured plates were subjected to shooting testsperformed using an AK47 7.62×39 mm Mild Steel Core (MSC) bulletmanufactured by Sellier & Belliot, Czech Republic. The first shot wasfired at a projectile speed at which it is anticipated that 50% of theshots would be stopped (V₅₀ value). The actual bullet speed was measuredat a short distance before impact. If a stop was obtained, the next shotwas fired at an anticipated speed being 20 m/s higher than the previousspeed. If a perforation occurred, the next shot was fired at a speedbeing 20 m/s lower than the previous speed. The result for theexperimentally obtained V₅₀ value was determined using logisticalregression analysis. The kinetic energy of the bullet at V₅₀ was dividedby the total areal density of the plate, thus reaching the so-called SEAvalue.

TABLE 1 Results of the anti-ballistic testing Comparative Example 1Experiment A SEA (J/Kg/m²) 157 145 Density (g/cm³) 0.952 0.959

The results from Table 1 illustrate that the combination of a reducedatmospheric environment in combination with high pressure results in animprovement in SEA of about 8%. The results also confirm that the use ofa reduced atmospheric pressure environment in combination with highpressure produces a similar densification effect as the degassing stepin the comparative example, which is the conventional approach toconsolidating a stack as taught in GB 2253420.

Dimensional Stability.

Twenty two panels were produced and tested according to Example 1 to 3and the corresponding comparative experiments. Half of the panels (11panels) were tested for anti-ballistic performance (without thermalconditioning), as described above. The other half of the panels wereeach marked at 16 positions in a grid equally spaced 10 cm apart and 5cm from the edges (or the equivalent ratio thereof). The panels werematched such that adjacent panels cut form the same main panel were usedto pair anti-ballistic and dimensional stability results. The originalthickness of the panel at each of the predefined position were measured,with the variation across the panels found to be less than 1% (or lessthan 0.2mm) and in most instances less than 0.5% (less than 0.1 mm). Thepanels were placed on trays in an oven set at 90° C. for 160 hours(thermal conditioning). At regular intervals of no less than 24 hours,the panels were removed from the oven and the thickness of thepredefined positions measured. In addition, the maximum thickness of anyposition on the board was also measured. The panel thickness wasmeasured and returned to the oven within 10 minutes and preferablywithin 5 minutes of the panels being removed from the oven formeasurement. Under this procedure, the temperature of the panels whenmeasured is considered to be about the same as temperature in the oven(i.e. about 90° C.). This process was repeated until the maximum %increase in thickness had reached a maxima.

The change in the average thickness and maximum panel thickness wasdetermined from the measurement data. It was observed that the maximumpanel thickness was recorded in the central portion of the panels withthe dimensional change increasing from the predefined positions aroundthe periphery to the 4 central predefined positions. A graph correlatingthe relationship between dimensional stability (maximum thicknessincrease (ΔT)) and anti-ballistic performance is provided in FIG. 1.

The results (FIG. 1) indicate that the application the application ofpressure and vacuum to a stack of sheets during the consolidation stepof the present invention, results in articles having improvedanti-ballistic performance in addition to improved dimensionalstability. Indeed, for conventional anti-ballistic articles to beproduced with comparable anti-ballistic performance then a consolidationpressure of 30 MPa is required compared to only 16.5 MPa using thevacuum technology of the present invention (compare comparativeexperiment B-2 and example 3-1). However, even when conventionalarticles are produced with equivalent anti-ballistic performance to thatof the present invention, the associated dimensional stability is onlyabout half that of the articles produced under the scope of the presentinvention (FIG. 1). Thus, the articles produced under the scope of thepresent invention are distinct from conventional articles.

Surprisingly, this technical effect is not seen at lower pressuresoutside the scope of the present invention and, in fact, vacuum appliedat lower pressures (2.0 MPa) actually leads to a slight decrease inanti-ballistic performance (D-1, D-2 and E-1).

1. An anti-ballistic article comprising a stack of sheets, each sheetcomprising one or more mono-layers of polyethylene anti-ballistic fibersand a thermoplastic binder, wherein the specific energy absorption (SEA)of the anti-ballistic article is greater than 145 J/kg/m² and themaximum % thickness increase, measured at about 90° C., is less than 8%after storing the article for 160 hours at 90° C.
 2. The anti-ballisticarticle according to claim 1, wherein the specific energy absorption(SEA) of the anti-ballistic article is greater than 147 J/kg/m².
 3. Theanti-ballistic article according to claim 1, wherein the specific energyabsorption (SEA) of the anti-ballistic article is greater than 151J/kg/m².
 4. The anti-ballistic article according to claim 1, wherein thespecific energy absorption (SEA) of the anti-ballistic article isgreater than 153J/kg/m².
 5. The anti-ballistic article according toclaim 1, wherein the maximum % thickness increase, measured at about 90°C., is less than 7.5% after storing the article for 160 hours at 90° C.6. The anti-ballistic article according to claim 5, wherein the maximum% thickness increase, measured at about 90° C., is less than 7.0% afterstoring the article for 160 hours at 90° C.
 7. The anti-ballisticarticle according to claim 5, wherein the maximum % thickness increase,measured at about 90° C., is less than 6.5% after storing the articlefor 160 hours at 90° C.
 8. The anti-ballistic article according to claim5, wherein the maximum % thickness increase, measured at about 90° C.,is less than 6.0% after storing the article for 160 hours at 90° C. 9.The anti-ballistic article according to claim 1, wherein the weight perunit area of the anti-ballistic fiber in the sheet or monolayer rangesfrom 5 to 250 g/m².
 10. The anti-ballistic article according to claim 1,the article comprising at least 40 sheets.
 11. The anti-ballisticarticle according to claim 1, wherein the polyethylene anti-ballisticfibers are in the form of tapes.
 12. The anti-ballistic articleaccording to claim 1, wherein the amount of thermoplastic binder is lessthan 20wt %.
 13. The anti-ballistic article according to claim 12wherein the thermoplastic binder is chosen from thermoplastic polymerpolyurethanes, polyvinyls, polyacrylics, polyolefins and thermoplasticelastomeric block copolymers,polyisopropene-polyethylene-butylene-polystyrene,polystyrene-polyisoprene-polystyrene block copolymers.
 14. Theanti-ballistic article according to claim 12 wherein the thermoplasticbinder binder has a tensile modulus (determined in accordance with ASTMD638, measured at 25° C.) of at least 250 MPa.
 15. The anti-ballisticarticle according to claim 1, wherein the article has an areal densityof at least 2 kg/m².
 16. The anti-ballistic article according to claim15, wherein the areal density of the article is at least 6 kg/m². 17.The anti-ballistic article according to claim 15, wherein the arealdensity of the article is at least 15 kg/m².
 18. The anti-ballisticarticle according to claim 1, wherein the fibers in a mono-layer areunidirectionally oriented.
 19. The anti-ballistic article according toclaim 1, wherein the fibers in a mono-layer are woven.
 20. Theanti-ballistic article according to claim 18, further comprising atleast one woven sheet with anti-ballistic fibers.